dc.contributor.advisorNasar, Ricardo Silveirapt_BR
dc.contributor.authorBezerra, Maria José Oliveira da Silvapt_BR
dc.date.accessioned2014-12-17T15:42:27Z-
dc.date.available2007-11-06pt_BR
dc.date.available2014-12-17T15:42:27Z-
dc.date.issued2007-09-17pt_BR
dc.identifier.citationBEZERRA, Maria José Oliveira da Silva. Síntese e caracterização da ferrita de MnZn obtida pelo método dos citratos precursores. 2007. 114 f. Dissertação (Mestrado em Físico-Química; Química) - Universidade Federal do Rio Grande do Norte, Natal, 2007.por
dc.identifier.urihttps://repositorio.ufrn.br/jspui/handle/123456789/17778-
dc.description.abstractIt was synthesized MnZn ferrite with general formulae Mn1-xZnxFe2O4 (mol%), 0,3 &#8804; x &#8804; 0,7 by using the citrate precursor method. The precursors decomposition was studied by thermogravimetric analysis (TGA), differential thermogravimetric analysis (DTG), differential thermal analysis (DTA) and Fourier transform infrared (FTIR) of powder calcined at 350ºC/3,5h. X-ray diffraction pattern (XRD) of samples was done from 350 to 1200ºC/2h using various atmospheres. The power calcined at 350ºC/3,5h formed spinel phase. It is necessary atmosphere control to avoid secondary phase such as hematite. From 900 to 1200ºC was obtained 90,66 and 100% of MnZn spinel ferrite phase, respectively. Analysis by dispersive energy scanning (EDS) at 350ºC shows high Mn and Zn dispersion, indicating that the diffusion process was homogeneous. Semi-quantitative analysis by EDS verified that despite the atmosphere control during calcinations at high temperatures (< 800ºC) occurred ZnO evaporation causing stoichiometric deviation. Vibrating sample magnetometer (VSM) measures show soft ferrite material characteristics with Hc from 6,5 x 10-3 to 11,1 x 10-2 T. Saturation magnetization (Ms) and initial permeability (µi) of MnZn spinel phase obtained, respectively, from 14,3 to 83,8 Am2/kg and 14,1 to 62,7 (Am2/kg)Teng
dc.description.sponsorshipConselho Nacional de Desenvolvimento Científico e Tecnológicopt_BR
dc.formatapplication/pdfpor
dc.languageporpor
dc.publisherUniversidade Federal do Rio Grande do Nortepor
dc.rightsAcesso Abertopor
dc.subjectFerritapor
dc.subjectMétodo Citrato Precursorpor
dc.subjectFase Espinéliopor
dc.subjectFerriteseng
dc.subjectCitrate precursor methodeng
dc.subjectSpinel phaseeng
dc.titleSíntese e caracterização da ferrita de MnZn obtida pelo método dos citratos precursorespor
dc.typemasterThesispor
dc.publisher.countryBRpor
dc.publisher.initialsUFRNpor
dc.publisher.programPrograma de Pós-Graduação em Químicapor
dc.contributor.authorIDCPF:02299260455por
dc.contributor.authorLatteshttp://lattes.cnpq.br/3998255731105471por
dc.contributor.advisorIDCPF:02168290890por
dc.contributor.advisorLatteshttp://lattes.cnpq.br/9213856023536973por
dc.contributor.advisor-co1Nasar, Marinalva Cerqueirapt_BR
dc.contributor.advisor-co1IDCPF:04460759810por
dc.contributor.advisor-co1Latteshttp://lattes.cnpq.br/9366338897724607por
dc.contributor.referees1Araújo, José Humberto dept_BR
dc.contributor.referees1IDCPF:24150720444por
dc.contributor.referees1Latteshttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4785558U2por
dc.contributor.referees2Acchar, Wilsonpt_BR
dc.contributor.referees2IDCPF:50580396720por
dc.contributor.referees2Latteshttp://lattes.cnpq.br/5460040602567184por
dc.contributor.referees3Rezende, Mirabel Cerqueirapt_BR
dc.contributor.referees3IDCPF:03513454856por
dc.contributor.referees3Latteshttp://lattes.cnpq.br/3744737176516322por
dc.description.resumoFoi sintetizada ferrita de MnZn com fórmula geral Mn1-xZnxFe2O4 (mol%) para 0,3 &#8804; x &#8804; 0,6 com uso do método dos citratos precursores. A decomposição dos precursores foi estudada por análise termogravimétrica (TGA), termogravimétrica diferencial (DTG), análise térmica derivada (DTA) e espectroscopia na região do infravermelho (FTIR) dos pós calcinados em 350°C/3,5h. Foram feitas difrações de raios X (DRX) entre 350 e 1200ºC/2h usando várias atmosferas. O pó calcinado a 350ºC/3,5h formou fase espinélio. É necessário o controle da atmosfera para evitar fases secundárias como a hematita. Em 900 e 1200ºC foram obtidos respectivamente, 90,7 e 100% de fase ferrita espinélio. Análises por espectroscopia de energia dispersiva (EDS) em 350ºC mostrou alta dispersão de Mn e Zn, indicando que o processo de difusão foi homogêneo. A análise semi-quantitativa por EDS verificou que apesar do controle da atmosfera durante a calcinação em altas temperaturas (> 800ºC), ocorreu vaporização de ZnO causando desvio estequiométrico. Medidas por magnetômetro de amostra vibrante (MAV) mostraram características de materiais magneticamente macios com Hc de 6,5 x 10-3 até 11,1 x 10-2 T. A magnetização de saturação e a permeabilidade inicial da fase espinélio de MnZn foi obtida entre 14,3 a 83,8 Am2/kg e 14,1 a 62,7 (Am2/kg)T, respectivamentepor
dc.publisher.departmentFísico-Química; Químicapor
dc.subject.cnpqCNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICApor
Appears in Collections:PPGQ - Mestrado em Química

Files in This Item:
File Description SizeFormat 
MariaJOSB.pdf5,31 MBAdobe PDFThumbnail
View/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.