dc.contributor.authorAlves Júnior, Clodomiro-
dc.contributor.authorLima, José de Anchieta-
dc.contributor.authorHajek, Vaclav-
dc.contributor.authorCunha, João Batista Marimon-
dc.contributor.authorSantos, Carlos Alberto-
dc.identifier.citationSurface & Coatings Technology 201 (2007) 7566–7573pt_BR
dc.description.abstractIn this work, AISI 1010 steel samples were plasma nitrided into 20% N 2 100 Pa and 400 Pa for N 2 and H 2 , respectively), temperatures of 500 and 580 °C, during 2 h. Three different procedures for cooling were accomplished after nitriding. In the first procedure the cooling occurred naturally, that is, the sample was kept on substrate holder. In the second one the sample was pulled off and cooling in a cold surface. Finally, in the third cooling process the sample was pulled off the substrate holder down into special reservoir filled with oil held at ambient temperature. The properties of the AISI 1010 steel samples were characterized by optical and electron microscopy, X-ray diffraction, Mössbauer spectroscopy and microhardness tests. Thermal gradient inside the sample kept on substrate holder during cooling process was measured by three inserted thermocouples at different depths. When samples were cooled rapidly the transformation of ϵ-Fe 2 − 3 N to γ′-Fe 4 N was inhibited. Such effect is indicated by the high concentration of ϵ-Fe compound zone. To get solid state solution of nitrogen in the diffusion zone, instead of precipitates of nitride phases, the cooling rate should be higher than a critical value of about 0.95 °C/s. When this value is reached at any depth of the diffusion zone, two distinct diffusion zones will appear. Temperature gradients were measured inside the samples as a consequence of the plasma treatment. It's suggested the need for standardization of the term “treatment temperature” for plasma treatment because different nitrided layer properties could be reported for the same “treatment temperature”.pt_BR
dc.description.sponsorshipCapes e CNPqpt_BR
dc.rightsAcesso Abertopt_BR
dc.subjectCooling ratept_BR
dc.subjectplasma nitridingpt_BR
dc.subjectAISI 1010pt_BR
dc.subjectThermal gradientpt_BR
dc.titleEffect of cooling rate on properties of plasma nitrided AISI 1010 steelpt_BR
Appears in Collections:CT - DEM - Artigos publicados em periódicos

Files in This Item:
File Description SizeFormat 
Effect of cooling rate on properties of plasma nitrided AISI 1010 steel.pdf2.33 MBAdobe PDFThumbnail

This item is licensed under a Creative Commons License Creative Commons