Estudo do aproveitamento de resíduos PAE no desenvolvimento de materiais cerâmicos

Abstract

This work presents a new ceramic material obtained through the incorporation of solid waste from the steel industry and known as dedusting powder PAE - in ceramic formulations based on clay, potassium and sodium feldspars, kaolin and talc. Formulations were prepared with ceramic residue levels of 0% (basic mass - MB), 2%, 4% and 8%, subjected to firing at temperatures of 1000 ° C, 1050ºC, 1100ºC and 1150ºC for periods of 15 min. and 120 min. The physicchemical and mechanical properties of these ceramic formulations were determined based on the firing temperature, residence time in the oven and the percentage of waste. Since the physicochemical and mechanical properties of the sintered materials were evaluated by chemical analysis techniques (fluorescence X-rays - FRX), particle size distribution, specific surface area, apparent density, structural analysis by diffraction of X-rays (DRX) and characterization of surface by scanning electron microscopy (SEM). The magnetic response characteristics and the pattern of magnetic ferrites of the samples were analyzed in the assay conditions, having noticed that the saturation magnetic susceptibility depend on the sintering temperature of the material and it is associated with its crystal structure. From the analysis results, it was concluded that the ceramic material with better physical and mechanical properties is obtained when the 8% from PAE residue is added to standard formulation under the burn time of 15 minutes and temperature of 1150ºC.