Use este identificador para citar ou linkar para este item:
https://repositorio.ufrn.br/handle/123456789/33243| Título: | Fracture toughness evaluation of WC–10 wt% Co hardmetal sintered under high pressure and high temperature |
| Autor(es): | Mashhadikarimi, Meysam Gomes, Uílame Umbelino Oliveira, M. P. Guimarães, R. D. S. Mello Júnior, M. M. B. Filgueira, Marcello |
| Palavras-chave: | Hardmetals;High pressure;High temperature;Fracture toughness;Grain growth;WC |
| Data do documento: | 29-Nov-2016 |
| Editor: | Taylor and Francis Group |
| Referência: | KARIMI, M. M.; GOMES, U. U.; OLIVEIRA, M. P.; GUIMARÃES, R. D. S.; MELLO, M. M. B.; FILGUEIRA, M. Fracture toughness evaluation of WC–10 wt% Co hardmetal sintered under high pressure and high temperature. High Pressure Research, [S.L.], v. 37, n. 1, p. 59-69, 29 nov. 2016. Disponível em: https://www.tandfonline.com/doi/abs/10.1080/08957959.2016.1261403?journalCode=ghpr20. Acesso em: 23 mar. 2021. http://dx.doi.org/10.1080/08957959.2016.1261403. |
| Resumo: | This work focused on fracture toughness studies of WC–10 wt% Co hardmetal fabricated through the high pressure/high-temperature technique. A powder mixture of WC–10 wt% Co was sintered at 1500–1900°C under a pressure of 7.7 GPa for 2 and 3 min. Vickers hardness test at two different loads of 15 and 30 kgf was done and fracture toughness of the sintered bodies was measured using the indentation method to obtain the effect of sintering parameters. Structural analyses were also performed via X-ray diffraction to investigate structure-related properties. Full density was achieved for high sintering temperature along with abnormal grain growth that reduced hardness. High hardness was observed ranging from 1200 to 1670 HV and fracture toughness increased with increasing sintering temperature up to the highest value of 17.85 MPa/m |
| URI: | https://repositorio.ufrn.br/handle/123456789/33243 |
| ISSN: | 0895-7959 1477-2299 |
| Aparece nas coleções: | CCET - DFTE - Artigos publicados em periódicos CT - DEMAT - Artigos publicados em periódicos |
Arquivos associados a este item:
| Arquivo | Descrição | Tamanho | Formato | |
|---|---|---|---|---|
| FractureToughnessEvaluation_MASHHADIKARIMI_2017.pdf | 2,24 MB | Adobe PDF | Visualizar/Abrir |
Este item está licenciada sob uma Licença Creative Commons