Borges, Boniek Castillo DutraSouza, Bárbara Beatriz Teixeira Lima Cardoso de2023-11-102023-11-102023-07-20SOUZA, Bárbara Beatriz Teixeira Lima Cardoso de. Efeito da incorporação de xilitol na dureza de superfície de um compósito bulk fill fluido. Orientador: Dr. Boniek Castillo Dutra Borges. 2023. 26f. Dissertação (Mestrado em Ciências Odontológicas) - Centro de Ciências da Saúde, Universidade Federal do Rio Grande do Norte, Natal, 2023.https://repositorio.ufrn.br/handle/123456789/55293Introduction: In view of the need for improved longevity of restorations, the development of antimicrobial resins has become necessary. Xylitol, a natural and biocompatible antimicrobial compound, may be a potential additive to include this property in a flowable bulk fill resin without compromising its integrity. Objective: To evaluate the surface microhardness of an antimicrobial resin developed by adding xylitol (0% or control; 2.5%; 5%) to a commercial flowable bulk fill resin (Tetric N-Flow Bulk Fill, Ivoclar Vivadent, Schaan, Liechtenstein). Methodology: 3 groups (n=12) were obtained by changing the xylitol concentration (0% or control; 2.5%; 5%). To obtain the experimental resins, xylitol powder was incorporated into the flowable resin by manual spatulation for 1 min in a darkroom. Based on an acrylic mold, 5 mm diameter disks were made by curing of a single increment with a 1400 mW/cm² irradiance LED device (Bluephase, Ivoclar Vivadent) for 10s. The disks were subjected to Vickers microhardness analysis (HMV-2, Shimadzu, Tokyo, Japan) on the upper face, with a static load of 300g and in a time of 10 s, obtaining an mean after three indentations for sample. Statistical analysis was performed using one-way ANOVA and Tukey's test for comparison between groups (p < 0.05). Results: The 5% xylitol group showed lower mean surface microhardness when compared to the 0% and 2.5% groups. Conclusion: Xylitol negatively affected restoration hardness mainly when a 5% concentration was used (p < 0.01).Acesso AbertoXilitolAntimicrobianosCárie dentáriamasterThesisCNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA