Navegando por Autor "Paz, Renê Anisio da"
Agora exibindo 1 - 3 de 3
- Resultados por página
- Opções de Ordenação
Artigo Effect of molecular weight of Polyamide 6 in rheological properties of nanocomposites with Brazilian organoclay(Trans Tech Publications, 2016-08-31) Leite, Amanda Melissa Damião; Paz, Renê Anisio da; Araújo, Edcleide Maria; Melo, Tomás Jeferson Alves; Pessan, Luiz Antônio; Passsador, Fábio RoebrtoPolyamide 6 (PA6)/Brazilian organoclay nanocomposites were obtained by melt intercalation and the structural and rheological properties were studied. The nanoclay was treated with quaternary ammonium salt (Cetremide) and characterized using infrared spectroscopy (FTIR) and X-ray diffraction (XRD). The results indicated the effective organophilization of nanoclay. The nanocomposites were obtained by melt intercalation using a twin screw corrotacional extruder in two steps. Firstly, a masterbatch of PA6/nanoclay (1:1) was prepared. In the second step the masterbatch was diluted in PA6 to obtain 3 and 5 wt% of nanoclay in the nanocomposites. The specimens were injection molded and analyzed using capillary rheometry, X-ray diffraction and transmission electron microscopy (TEM). The results of capillary rheometry showed that the presence of the organoclay in PA6 increased the viscosity of the systems. Structural characterization showed that the nanocomposites were predominant in exfoliated structureArtigo Mechanical and thermomechanical properties of polyamide 6/Brazilian organoclay nanocomposites(Associação Brasileira de Polímeros, 2016) Leite, Amanda Melissa Damião; Paz, Renê Anisio da; Araújo, Edcleide Maria; Medeiros, Vanessa da Nóbrega; Melo, Tomás Jeferson Alves de; Pessan, Luiz AntônioPolymer/clay nanocomposites are a new class of composites with polymer matrices where the disperse phase is a silicate with elementary particles that have at least one of dimensions in nanometer order. Polyamide 6/Brazilian organoclay nanocomposites were prepared by melt intercalation, and the mechanical, thermal and thermomechanical properties were studied. The structure and morphology of the nanocomposites were evaluated by X-ray diffraction (XRD) and transmission electron microscopy (TEM). It was verified by XRD and TEM analysis that all systems presented exfoliated structure predominantly. By thermogravimetry (TG), nanocomposites showed higher stabilities in relation to pure polymer. It was observed that the nanocomposites showed better mechanical properties compared to the properties of polyamide 6. The heat deflection temperature (HDT) values of the nanocomposites showed a significant increase in relation to pure polymerTCC Obtenção e caracterização de membranas de nanocompósitos de poliamida 6 e argila a partir de solvente aquoso(Universidade Federal do Rio Grande do Norte, 2021-04-23) Alves, Juliana Isa Pereira; Leite, Amanda Melissa Damião; Marciano Furukava; Viana, Kaline Melo do Souto; Paz, Renê Anisio daO número de pesquisas na área de membranas vem aumentando constantemente por ser um material que exerce um importante papel na área de separação. As membranas podem ser divididas em dois grandes grupos: as densas e porosas e, de acordo com as suas características morfológicas, elas ainda podem ser divididas em anisotrópicas ou isotrópicas. Como objeto de estudo desta pesquisa, foram analisadas as membranas sintéticas de poliamida 6 (PA6) e de nanocompósito de PA6 com diferentes teores de argila nacional (1%, 3% e 5%), obtidas através do método de inversão de fases por precipitação de solvente. O solvente usado foi o ácido fórmico 85%, que possui um maior teor de água em sua composição. As amostras foram caracterizadas a partir das análises de Espectrometria de Infravermelho com Transformada de Fourier (FTIR), Difração de Raio-X (DRX), Microscopia Eletrônica de Varredura (MEV) e Permeação a Vapor. Através do método de DRX, foi possível observar o pico característico do material, referente a poliamida 6, que é considerado um polímero semicristalino. Observou-se também que algumas amostras apresentaram uma estrutura esfoliada ou parcialmente esfoliada. Com os dados do MEV, pôde-se analisar como estava a distribuição dos poros e o impacto que a concentração de argila teve na morfologia da membrana. Por meio dos dados do FTIR, foi possível detectar a presença de argila e analisar se ela modificou a banda característica do polímero. Por último, com o ensaio de permeação a vapor, observou-se que a presença da argila foi favorável para o aumento da permeabilidade. Sendo assim, através das análises realizadas, foi possível identificar a composição que teve um melhor desempenho.