Logo do repositório
  • Página Inicial(current)
  • Buscar
    Por Data de PublicaçãoPor AutorPor TítuloPor Assunto
  • Tutoriais
  • Documentos
  • Sobre o RI
  • Eventos
    Repositório Institucional da UFRN: 15 anos de conexão com o conhecimento
  • Padrão
  • Amarelo
  • Azul
  • Verde
  • English
  • Português do Brasil
Entrar

SIGAA

  1. Início
  2. Pesquisar por Autor

Navegando por Autor "Rodrigues, H. A. B."

Filtrar resultados informando as primeiras letras
Agora exibindo 1 - 2 de 2
  • Resultados por página
  • Opções de Ordenação
  • Carregando...
    Imagem de Miniatura
    Artigo
    Anisotropy field and transverse susceptibility in nanocrystalline hexaferrites
    (Physica B: Condensed Matter, 2006-10-01) Araújo, José Humberto de; Soares, J. M.; Machado, F. L. A.; Cabral, F. A. O.; Rodrigues, H. A. B.; Ginani, Marconi Floripe
    Nanocrystalline strontium and barium hexaferrites were produced by an ionic coordination reaction method. The average particle size obtained using the Rietveld X-ray refinement technique and by scanning electron microscopy was quite uniform and close to 50 nm. Transverse susceptibility measurements yielded both the coercive and the anisotropy magnetic fields. The results were analysed using a theoretical model proposed by Aharoni et al. [Bull. Res. Counc. Isr. A 6 (1957) 215]. This overall procedure seems to be quite useful in determining the distribution of the anisotropy magnetic fields in granular materials
  • Nenhuma Miniatura disponível
    Artigo
    Anisotropy field and transverse susceptibility in nanocrystalline hexaferrites
    (Elsevier, 2006-10-01) Araujo, Jose Humberto; Soares, J. M.; Machado, F. L. A.; Cabral, F. A. O.; Rodrigues, H. A. B.; Ginani, Marconi Floripe
    Nanocrystalline strontium and barium hexaferrites were produced by an ionic coordination reaction method. The average particle size obtained using the Rietveld X-ray refinement technique and by scanning electron microscopy was quite uniform and close to 50 nm. Transverse susceptibility measurements yielded both the coercive and the anisotropy magnetic fields. The results were analysed using a theoretical model proposed by Aharoni et al. [Bull. Res. Counc. Isr. A 6 (1957) 215]. This overall procedure seems to be quite useful in determining the distribution of the anisotropy magnetic fields in granular materials.
Repositório Institucional - UFRN Campus Universitário Lagoa NovaCEP 59078-970 Caixa postal 1524 Natal/RN - BrasilUniversidade Federal do Rio Grande do Norte© Copyright 2025. Todos os direitos reservados.
Contato+55 (84) 3342-2260 - R232Setor de Repositórios Digitaisrepositorio@bczm.ufrn.br
DSpaceIBICT
OasisBR
LAReferencia
Customizado pela CAT - BCZM