dc.identifier.citationGALVÃO, M. R. et al. Compressive strength of dental composites photo-activated with different light tips. Laser Physics, v. 23, n. 4, p. 045604, 2013.pt_BR
dc.rightsAcesso Abertopt_BR
dc.subjectcompound microhybridpt_BR
dc.subjectresistant restorationspt_BR
dc.subjectdental composite photopt_BR
dc.titleCompressive strength of dental composites photo-activated with different light tipspt_BR
dc.description.resumoThe aim of this study was to evaluate the compressive strength of microhybrid (FiltekTM Z250) and nanofilled (FiltekTM Supreme XT) composite resins photo-activated with two different light guide tips, fiber optic and polymer, coupled with one LED. The power density was 653 mW cm−2 when using the fiber optic light tip and 596 mW cm−2 with the polymer. After storage in distilled water at 37 ± 2 "C for seven days, the samples were subjected to mechanical testing of compressive strength in an EMIC universal mechanical testing machine with a load cell of 5 kN and speed of 0.5 mm min−1. The statistical analysis was performed using ANOVA with a confidence interval of 95% and Tamhane’s test. The results showed that the mean values of compressive strength were not influenced by the different light tips (p > 0.05). However, a statistical difference was observed (p < 0.001) between the microhybrid composite resin photo-activated with the fiber optic light tip and the nanofilled composite resin. Based on these results, it can be concluded that microhybrid composite resin photo-activated with the fiber optic light tip showed better results than nanofilled, regardless of the tip used, and the type of the light tip did not influence the compressive strength of either composite. Thus, the presented results suggest that both the fiber optic and polymer light guide tips provide adequate compressive strength to be used to make restorations. However, the fiber optic light tip associated with microhybrid composite resin may be an interesting option for restorations mainly in posterior teeth.pt_BR
Appears in Collections:CCS - DOD - Artigos publicados em periódicos

Files in This Item:
File Description SizeFormat 
CompressiveStrengthDental_Galvao_2013.pdf206.96 kBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.