Título:	Correlation between vertical misfits and stresses transmited to implants from metal frameworks
Autor(es):	Torres, Érica Miranda Barbosa, Gustavo Augusto Seabra Bernardes, Sérgio Rocha Mattos, Maria da Gloria Chiarello de Ribeiro, Ricardo Faria
Palavras-chave:	Fixed implant prosthesis;Dental implants;Marginal misfit;Dental alloys;Photoelastic analysis
Data do documento:	2011
Referência:	TORRES, Érica Miranda et al. Correlation between vertical misfits and stresses transmited to implants from metal frameworks. Journal of Biomechanics, v. 44, p. 1735-1739, 2011.
Resumo:	An inappropriate prosthetic fit could cause stress over the interface implant/bone. The objective of this study was to compare stresses transmitted to implants from frameworks cast using different materials and to investigate a possible correlation between vertical misfits and these stresses. Fifteen one-piece cast frameworks simulating bars for fixed prosthesis in a model with five implants were fabricated and arranged into three different groups according to the material used for casting: CP Ti (commercially pure titanium), Co-Cr (cobalt-chromium) or Ni-Cr-Ti (nickel-chromium-titanium) alloys. Each framework was installed over the metal model with all screws tightened to a 10 N cm torque and then, vertical misfits were measured using an optical microscope. The stresses transmitted to implants were measured using quantitative photoelastic analysis in values of maximum shear stress (τ), when each framework was tightened to the photoelastic model to a 10 N cm standardized torque. Stress data were statistically analyzed using one-way ANOVA and Tukey's test and correlation tests were performed using Pearson's rank correlation (α = 0.05). Mean and standard deviation values of vertical misfit are presented for CP Ti (22.40 ± 9.05 μm), Co-Cr (66.41 ± 35.47 μm) and Ni-Cr-Ti (32.20 ± 24.47 μm). Stresses generated by Co-Cr alloy (τ = 7.70 ± 2.16 kPa) were significantly higher than those generated by CP Ti (τ = 5.86 ± 1.55 kPa, p = 0.018) and Ni-Cr-Ti alloy (τ = 5.74 ± 3.05 kPa, p = 0.011), which were similar (p = 0.982). Correlations between vertical misfits and stresses around the implants were not significant as for any evaluated materials.
URI:	https://repositorio.ufrn.br/jspui/handle/123456789/23911