Aproveitamento sustentável do bagaço de cana de açúcar para obtenção do acetato de celulose

Abstract

The sustainable use of waste resulting from the agribusiness is currently the focus of research, especially the sugar cane bagasse (BCA), being the lignocellulosic waste produced in greater volume in the Brazilian agribusiness, where the residual biomass has been applied in production energy and bioproducts. In this paper, pulp was produced in high purity from the (BCA) by pulping soda / anthraquinone and subsequent conversion to cellulose acetate. Commercial cellulose Avicel was used for comparison. The obtained cellulose acetate was homogeneous acetylation reaction by modifying the variables, the reaction time in hours (8, 12, 16, 20 and 24) and temperature in ° C (25 and 50). FTIR spectra showed characteristic bands identical to cellulosic materials, demonstrating the efficiency of separation by pulping. The characterization of cellulose acetate was obtained and by infrared spectroscopy (FTIR), X-ray diffraction (XRD), thermogravimetric analysis (TG / DTG / DSC), scanning electron microscopy (SEM) and determining the degree of substitution (DS ) for the cellulose acetate to confirm the acetylation. The optimal reaction time for obtaining diacetates and triacetates, at both temperatures were 20 and 24 h. Cellulose acetate produced BCA presented GS between 2.57 and 2.7 at 25 ° C and 50 ° C GS obtained were 2.66 and 2.84, indicating the actual conversion of cellulose BCA of di- and triacetates. Comparative mode, commercial cellulose Avicel GS showed 2.78 and 2.76 at 25 ° C and 2.77 to 2.75 at 50 ° C. Data were collected in time of 20 h and 24 h, respectively. The best result was for the synthesis of cellulose acetate obtained from the BCA GS 2.84 to 50 ° C and 24 hours, being classified as cellulose triacetate, which showed superior result to that produced with the commercial ethyl cellulose Avicel, demonstrating converting potential of cellulose derived from a lignocellulosic residue (BCA), low cost, prospects of commercial use of cellulose acetate