Estruturas cerâmicas a base de zircônia e alumina utilizadas na confecção de infra - estruturas para coroas e pontes fixas

Abstract

The continuous advances in ceramic systems for crowns and bridges infrastructure getting researchers and manufacturers looking for a material that has good mechanical properties and aesthetic. The purpose of this study was to verify in which composition and sintering temperature the ceramic system for infrastructure composed of alumina and zirconia would have the best mechanical properties. With this objective we made in UFRN laboratories 45 test bodies in the form of rectangular bars with the following dimensions: 30mm x 8mm x 3mm, where we separated by the sintering temperature: 1200°C, 1300ºC and 1400ºC, and by comp osition: 33% Zirconia + 67% Alumina; 50% Zirconia + 50% Alumina and 25% Zirconia + 75% Alumina, these test bodies were not infiltrated with glass. Also, were made nine test bodies by a technical from a laboratory with a commercial ceramic system: in the Ceram Zircônia (Vita - Zahnfabrik) with the following dimensions: 20mm x 10mm x 0.5mm, these test bodies following all recommendations of the manufacturer and were infiltrated with glass. Were realized optical and electronic microscopy analyses, hardness testing, resistance to bending in three points, porosity and bulk density. After analysis of the results we verified that with the increasing of sintering temperature, increased the value of resistance to bending, but with the same temperature there was no significant difference between the different compositions, samples made with the commercial ceramic that were infiltrated, presented a resistance to bending six times greater than the samples sintered to 1400°C and which have not been infiltra ted. There was no significant difference between the values of apparent porosity for the samples made in UFRN laboratories, but the samples of commercial ceramic obtained 0% in porosity apparent value. In tests of Rockwell Hardness there is an increase in the value of Hardness, with the increase of sintering temperature for the samples not infiltrated. Samples infiltrated showed similar values as the samples sintered in 1400°C. There was no significant difference between the values of apparent density among samples manufactured in UFRN laboratories and samples made with a commercial ceramic