Avaliação in vitro da razão base/topo de dureza e da resistência de união push-out entre uma resina composta contendo diatomita e uma resina composta bulk-fill

Abstract

The scarcity of data validating scientific diatomite benefits for physical properties of Zirconfill® resin composite makes essential to develop new studies, especially regarding the use of this resin composite containing diatomite in semi-direct restorations. Aim: To evaluate in vitro the cure and bond strength between a resin composite containing diatomite and a bulk-fill resin composite after 24 hours and after 06 months of water storage. Materials and methods: Twenty-eight bovine incisors (n=28) were used to produce conical dentinal cavities (4,8 mm of larger diameter x 2,8 mm of smaller diameter x 4 mm of thickness) and C-factor of magnitude 3.1. These cavities were restored with Filtek™ One Bulk-Fill (BF) (3M ESPE) or Zirconfill® (ZF) (BM4) resin composites, through the semi-direct technique, using Scotchbond™ Universal (3M ESPE) adhesive system and Relyx™ Ultimate (3M ESPE) dual resin cement. The cure analysis was performed through bottom-to-top (B/T) ratio of vickers hardness, while bond strength (RU) was performed through the push-out test in a universal testing machine. The specimens were stored in distilled water at 37 ºC for 24 hours or 06 months, but only RU analyzed the specimens after 06 months aging. B/T and RU data were, respectively, submitted to one-way and two-way analysis of variance (ANOVA) with Tukey's post-test (p <0.05). Results: There was no statistically significant difference between the composite resins in B/T. For RU, the ZF composite resin showed higher values than the BF resin at both evaluated times. However, there was no statistically significant difference in resin composites over time. Conclusion: The resin composite containing diatomite showed promise when used in semi-direct restorations since it obtained similar or even superior results to bulk-fill resin composite.